Preparation and osteocompatibility of hydroxyapatite coated on titanium from the reaction of sputtered CaO and vaporized P2O5.

TL;DRAbstract

Hydroxyapatite (HA) and other calcium phosphates were synthesized on titanium plates by a solid-gas state reaction of sputtered CaO and vaporized P(2)O(5). The calcium phosphates formed were HA, beta-tricalcium phosphate (beta-TCP; Ca(3)(PO(4))(2)), beta-calcium pyrophosphate (beta-PYR; Ca(2)P(2)O(7)), and beta-calcium metaphosphate (beta-MET; Ca(2)(PO(3))(2)). Their formation depended on the ratio of the sputtered CaO and the reacting P(2)O(5). For a mole ratio of CaO/P(2)O(5)=4 (Ca/P=2), an HA film was synthesized. The surface roughness increased by over seven times after the solid-gas state reaction from Ra = 0.16+/-0.02 microm (for the CaO film) to Ra = 1.15+/-0.25 microm (for the reacted film). The synthesized HA film-coated titanium plates and control non-coated titanium plates were implanted in the femora of two dogs for a period of two, four and 12 weeks, and observed using a soft X-ray radiograph and histological sections. New bone formation was observed without any connective

Chat with Paper

AI Agents for this Paper