Two-phase synthesis of olive-like NiS particles and chain-like Bi<sub>2</sub>S<sub>3</sub> nanowires
TL;DRAbstract
Abstract Highly dispersed olive-like NiS particles were synthesized in a liquid-liquid biphasic system at room temperature, where nickel xanthate in organic solvents (toluene and benzene) and sodium sulfide in water solution were used as nickel and sulfide sources, respectively. NiS particles were formed at the stabilized phase interface. The structures, chemical composition and optical characteristics of the products were investigated by transmission electron microscopy, scanning electron microscopy, X-ray photoelectron spectroscopy and ultraviolet-visible spectroscopy. The organic solvents obviously influenced the morphology of the NiS particles. The olive-like NiS with smooth surface and sharp ends was obtained at benzene/water interface, while spindle-like NiS particles with rough surface and circle ends were formed when using toluene as a solvent. Analogously, chainlike Bi 2 S 3 nanowires were produced at chloroform/water interface. The effect of the experiment parameters includin
Chat with Paper
AI Agents for this Paper
Abstract Highly dispersed olive-like NiS particles were synthesized in a liquid-liquid biphasic system at room temperature, where nickel xanthate in organic solvents (toluene and benzene) and sodium sulfide in water solution were used as nickel and sulfide sources, respectively. NiS particles were formed at the stabilized phase interface. The structures, chemical composition and optical characteristics of the products were investigated by transmission electron microscopy, scanning electron microscopy, X-ray photoelectron spectroscopy and ultraviolet-visible spectroscopy. The organic solvents obviously influenced the morphology of the NiS particles. The olive-like NiS with smooth surface and sharp ends was obtained at benzene/water interface, while spindle-like NiS particles with rough surface and circle ends were formed when using toluene as a solvent. Analogously, chainlike Bi 2 S 3 nanowires were produced at chloroform/water interface. The effect of the experiment parameters includin
Keywords
Chat
Click to start Chat