OMVPE growth and characterization of GaInAsSb for thermophotovoltaics

TL;DRAbstract

Studies on the materials development of Ga{sub 1{minus}x}In{sub x}As{sub y}Sb{sub 1{minus}y} alloys for thermophotovoltaic (TPV) devices are reviewed. Ga{sub 1{minus}x}In{sub x}As{sub y}Sb{sub 1{minus}y} epilayers were grown lattice matched to GaSb substrates by organometallic vapor phase epitaxy (OMVPE) using all organometallic precursors including triethylgallium, trimethylindium, tertiarybutylarsine, and trimethylantimony with diethyltellurium and dimethylzinc as the n- and p-type dopants, respectively. The overall material quality of these alloys depends on growth temperature, In content, V/III ratio, substrate misorientation, and to a lesser extent, growth rate. A mirror-like surface morphology and room temperature photoluminescence (PL) are obtained for GaInAsSb layers with peak emission in the wavelength range between 2 and 2.5 {micro}m. The crystal quality improves for growth temperature decreasing from 575 to 525 C, and with decreasing In content, as based on epilayer surface

Chat with Paper

AI Agents for this Paper