A new multiferroic Bi2FeMoO6 was synthesized by chemical route. The crystal structure was found to be distorted from cubic double perovskite structure, has rhombohedral symmetry. SEM reveals the formation of nanosized aggolomers and EDS confirms the material composition. Magnetic study shows the room temperature ferromagnetism. It also gives good co-existence of ferroelectricity at room temperature. These results suggests that the material can be envisaged as promising multiferroic material.
Chat with Paper
AI Agents for this Paper
A new multiferroic Bi2FeMoO6 was synthesized by chemical route. The crystal structure was found to be distorted from cubic double perovskite structure, has rhombohedral symmetry. SEM reveals the formation of nanosized aggolomers and EDS confirms the material composition. Magnetic study shows the room temperature ferromagnetism. It also gives good co-existence of ferroelectricity at room temperature. These results suggests that the material can be envisaged as promising multiferroic material.
Keywords
Chat
Click to start Chat