The influence of delayed light curing on the polymerization contraction stress and degree of conversion in dual-cured resin luting agents

TL;DRAbstract

The purpose of this study was 1) To determine the impact of eliminating or delaying the photo-activation procedure on the polymerization contraction stress (PCS)and degree of conversion (DC) of a dual-cured resin luting agent, and 2) To determine the amount of delay in photo-initiation of the dual-cured resin cements that can achieve a reduced PCS value with the highest possible DC. The amount of PCS and DC of a dual-cured resin luting agent was determined using a tensometer and ATR spectroscopic technique, respectively. Photo-activation delay in seven tested groups was 0 min, 2 min, 4 min, 6 min, 8 min, 10 min and no photoactivation. Five samples for each group were tested. There were two hypotheses for this study: 1) A significant decrease in the amount of PCS associated with delayed photo-activation, and 2) A significant increase in DC associated with delayed photo-activation.The PCS of the chemical-cure luting agent had significantly lower value than all of the light-cure groups. F

Chat with Paper

AI Agents for this Paper